HP Graphite Electrodes | |||||||
Aikin | Diamita (mm) | ||||||
300-400 | 450-500 | 550-700 | |||||
行业YB | 内控FC | 行业YB | 内控FC | 行业YB | 内控FC | ||
Resistivity μΩ.m≤ | Electrode | 7.0 | 6.2 | 7.5 | 6.2 | 7.5 | 6.2 |
Nono | 6.3 | 4.3 | 6.3 | 4.3 | 6.3 | 4.3 | |
Karfin Lankwasa (Mpa) ≥ | Electrode | 10.5 | 11.0 | 10.0 | 10.5 | 8.5 | 9.0 |
Nono | 17.0 | 18.0 | 17.0 | 18.0 | 17.0 | 18.0 | |
Na roba Modulus (Gpa) ≤ | Electrode | 14.0 | 9.0 | 14.0 | 9.0 | 14.0 | 9.0 |
Nono | 16.0 | 13.0 | 16.0 | 13.0 | 16.0 | 13.0 | |
Yawan yawa (g/cm³) | Electrode | 1.60 | 1.67 | 1.60 | 1.67 | 1.60 | 1.67 |
Nono | 1.72 | 1.77 | 1.72 | 1.77 | 1.72 | 1.77 | |
CTE(x10-6/℃)≤25℃-600℃ | Electrode | 2.4 | 2.2 | 2.4 | 2.0 | 2.4 | 2.0 |
Nono | 2.2 | 1.8 | 2.2 | 1.8 | 2.2 | 1.8 | |
Ash(%)≤ | Electrode | 0.5 | 0.3 | 0.5 | 0.3 | 0.5 | 0.3 |
Nono | 0.5 | 0.2 | 0.5 | 0.2 | 0.5 | 0.3 |
Izinin ƙarfin ƙarfin lantarki na lantarki | |||||||
Diamita mara kyau | Gudun iyawa mai izini (A) | Yawan wutar lantarki na yanzu | |||||
Millimeter | Inci | ||||||
300 | 12'' | 13000-17400 | 17-24 | ||||
350 | 14'' | 17400-24000 | 17-24 | ||||
400 | 16'' | 21000-31000 | 16-24 | ||||
450 | 18'' | 25000-40000 | 15-24 | ||||
500 | 20'' | 30000-48000 | 15-24 | ||||
550 | 22'' | 34000-53000 | 14-22 | ||||
600 | 24'' | 38000-58000 | 13-21 | ||||
650 | 26'' | 41000-65000 | 12-20 | ||||
700 | 28'' | 45000-72000 | 12-19 |
Babban juriya na yanzu da ƙimar fitarwa mai girma.
Kyakkyawan kwanciyar hankali mai girma kuma ba sauƙin lalacewa ba.
Juriya ga fatattaka da spalling.
High oxidation juriya da thermal girgiza juriya.
Babban ƙarfin injiniya da ƙarancin juriya.
High machining daidaici da kyau surface gama.
Tsarin Uniform, kyawawa mai kyau da haɓakar thermal